RECTANGULAR SECTION RINGS

-

RECTANGULAR SECTION RINGS

Rectangular section rings are widely used. They can generally be considered to be
interchangeable with elastomer O-rings. They may be manufactured by moulding
for high volumes but are also lathe cut from extruded tube.



A particular benefit ofrectangular rings is that they will not flex under cyclic pressure. They will therefore be less prone to leakage due to flexing and wear,  For this reason theyare used as an alternative to O-rings on some high duty hydraulic equipment and similar applications. Another familiar application is oil filters on automotive engines,where improved stability during fitting is an important consideration.

The rings may be of rectangular or square cross-section, depending on the application and
manufacturing methods.

O RING AND RECTANGULAR RINGS



 1. Without  compression
2. With Compression
3.With Compression and pressure activated.


사각형 단면 링이 널리 사용됩니다. 그들은 일반적으로

엘라스토머 O- 링과 호환 가능. 이들은 성형에 의해 제조 될 수있다.

높은 볼륨 용이지만 압출 튜브에서 선반 절단도 가능합니다.


직사각형 고리의 특별한 장점은 순환 압력 하에서는 사라지지 않는다는 것입니다. 그러므로 그들은 마모 및 마모로 인한 누출이 적습니다. 이러한 이유 때문에 일부 고 유압 장치 및 이와 유사한 어플리케이션에서 O- 링 대신 사용할 수 있습니다. 또 다른 친숙한 응용 분야는 피팅 중 향상된 안정성이 중요한 고려 사항 인 자동차 엔진의 오일 필터입니다.


링은 적용 분야에 따라 직사각형 또는 정사각형 단면 일 수 있습니다.

제조 방법.








Comments

Post a Comment

Popular posts from this blog

Calendering

-
Image
Introduction: Calendering is the process of making thin sheet of rubber and also lamination of such sheet on to other substrate like fabric,cord warp sheet by passing through set if rollers under controlled Conditions. A calendar comprises of a number of rows or bowls held in frame. Rolls rotate in opposite directions either with even speed or with a friction ratio. Types Of Rubber material used Elastomers that can be used include: ·          Neoprene ·          SBR ·          Natural ·          Hypalon ·          Urethane ·          EPDM          Viton           Fluroelastomer         Butyl          Nitrile         Silicone Fabric Materials Rayon Cotton Polyester Blends Monfilament Blends Kevlar Fiberglass Nylon Square Woeven Polyester Fiberglass Nomex ·        Advantage of Calendering: 1.Accurate rubber sheet gauge across the full length. 2.Frictioning operation for rubberized fabric 3.Skim coating
Read more

Types of Bridge Bearing

-
Image
Types of bridge bearing  1. Elastomeric Bearing a.Plain elastomer pads b.Laminated Elastomeric bearings 2.Sliding bearing Mechanism a. PTFE  sliding material b.Alternative sliding material 3.High load multi Rotational building: a.Pot bearing b.Disc bearing c.Spherical bearings 4. Fabricated steel mechanical bearing a.Rocker bearing b.Rocker cum rolling bearing Elastomeric Bearing: It consists of elastomer manufactured from synthetic or natural rubber and can take both translation and rotation movements through elastomer deformation. The ability of elastomer to carry large vertical loads is because of reinforcement provision that prevents lateral bulging of elastomer. There are number of elastomeric bearing pads classified based on types of reinforcements used. For example, steel reinforced, plain, fiberglass reinforced and cotton duck reinforced elastomeric bearing pads Strength and response of each type is different, steel reinforced ela
Read more

Shrinkage rate Calculation

-
I n Moulding process the rubber is Cured at high temperature and Pressure, the resulting Moulded parts are smaller in size than the actual. The Difference in the thermal expansion of the mold material result in shrink rate Shrink Rate= ( Cavity dimension- Part Length)/ Cavity dimension) (Typical units in/in) This shrinkage value is applied to the desired finished part size to “scale up” the cavity. The resulting cavity dimension is calculated as: Cavity Dimension= finished part length/ (1- Shrink rate) For example: Shrinkage rate testing was performed on a 70 Shore A Nitrile (Buna-N), Ethylene-Propylene (EP), Fluorosilicone (FVMQ), and 75 Shore A Fluorocarbon (FKM).  The Fluorosilicone and Fluorocarbon materials undergo a secondary vulcanization process called post-curing. During the post-curing process, the molded parts were baked in a ventilated oven at a specific time and temperature recommended by the material manufacturer, or at a temperature great
Read more